TOPAS® 6013F-04

环烯烃共聚物

Topas Advanced Polymers, Inc.

Technical Data

 

产品说明

Product Description

TOPAS 6013F-04 is a high temperature, general purpose film extrusion grade. It is a high clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and healthcare applications. It is used in monolayer and blended cast applications, and in coextrusions and blends in both cast and blown processes, for a wide variety of film and sheet products requiring excellent optics in applications such as heat resistant blister, hot fill, and easy tear packaging. If performance at elevated temperatures is not required, we also offer lower glass transition temperature (Tg) grades of TOPAS.

 

Selected Applications

• Pharmaceutical blisters 

• Decorative film and sheet 

• General packaging 

• Food packaging 

• Healthcare and food contact 

 

Leading Attributes

• Clarity, forming, barrier, heat resistance, halogen-free 

• Gloss, hardness, chemical resistance, forming 

• Easy or linear tear, heat resistance, hot fill 

• Not manufactured with BPA, phthalates, or halogens 

• Broad regulatory compliance 

 

Related Grades for Packaging and Film Extrusion

• TOPAS 5013F-04 - high temperature grade with higher flow

 

总体

 

材料状态 • 已商用：当前有效

资料 1 •  Processing (English)

•  Technical Datasheet (English)

搜索 UL 黄卡 •  Topas Advanced Polymers, Inc.

•  TOPAS®

供货地区 • 北美洲 • 拉丁美洲 • 亚太地区

• 非洲和中东 • 欧洲

• 纯度高 • 耐化学性良好 •

• 防潮 • 耐热性，高 无 BPA

特性 • 刚性，高 • 清晰度，高 • 无定形的

• 高光 • 食品接触的合规性 • 无卤

• 共聚物 • 通用

• 包装 • 流延薄膜 • 通用

用途 • 薄膜 • 片材 • 药品包装

• 混合 • 食品包装 • 医疗/护理用品

机构评级 • DMF 12132 • ISO 10993 • 欧洲 10/1/2011 12:00:00 AM

• FDA FCN 405 • USP 第VI类

形式 • 粒子

加工方法 • 薄膜挤出 • 共挤薄膜 • 热成型

• 吹塑薄膜 • 流延薄膜

物理性能 额定值(英制) 额定值(公制) 测试方法

密度 1.02g/cm³ 1.02g/cm³ ISO 1183

熔流率（熔体流动速率） (230°C/2.16 kg) 0.90g/10 min 0.90g/10 min ISO 1133

溶化体积流率（MVR） (230°C/2.16 kg) 0.0610in³/10min 1.00cm³/10min ISO 1133

吸水率 (饱和, 73°F (23°C)) 0.010% 0.010% ISO 62

薄膜 额定值(英制) 额定值(公制) 测试方法

薄膜厚度 - 经测试 2.8mil 70µm

 

TOPAS® 6013F-04

环烯烃共聚物

Topas Advanced Polymers, Inc.

薄膜 额定值(英制) 额定值(公制) 测试方法

拉伸模量 ISO 527-3/1

MD : 2.8 mil (70 µm), 铸造薄膜 348000psi 2400MPa

TD : 2.8 mil (70 µm), 铸造薄膜 326000psi 2250MPa

拉伸应力 ISO 527-3/50

MD : 断裂, 2.8 mil (70 µm), 铸造薄膜 7980psi 55.0MPa

TD : 断裂, 2.8 mil (70 µm), 铸造薄膜 6530psi 45.0MPa

伸长率 ISO 527-3/50

MD : 断裂, 2.8 mil (70 µm), 铸造薄膜 2.4% 2.4%

TD : 断裂, 2.8 mil (70 µm), 铸造薄膜 2.2% 2.2%

落锤冲击 (2.8 mil (70 µm), 铸造薄膜) < 36g < 36g ISO 7765-1

埃尔曼多夫抗撕强度 ISO 6383-2

MD : 2.8 mil (70 µm), 铸造薄膜 0.020lbf 0.088N

TD : 2.8 mil (70 µm), 铸造薄膜 0.020lbf 0.088N

透氧率 ASTM D3985

73°F (23°C), 2.8 mil (70 µm), 挤塑薄膜, 50% cm³•mil/100in²/at cm³•mm/m²/atm/

RH 72m/24 hr 2824 hr

水气透过率 ASTM F1249

2.8 mil (70 µm), 100°F (38°C), Cast Film, 90% g•mil/100in²/atm/ g•mm/m²/atm/24

RH 0.4024 hr 0.16hr

热性能 额定值(英制) 额定值(公制) 测试方法

玻璃转化温度 280°F 138°C ISO 11357-2

光学性能 额定值(英制) 额定值(公制) 测试方法

光泽度 (60°, 2.76 mil (70.0 µm), 铸造薄膜) > 100 > 100 ISO 2813

雾度 (2.76 mil (70.0 µm), 铸造薄膜) < 1.0% < 1.0% ISO 14782

挤出 额定值(英制) 额定值(公制)

挤塑机进料部分 68 到 158°F 20 到 70°C

料筒1区温度 446 到 464°F 230 到 240°C

料筒2区温度 482 到 500°F 250 到 260°C

料筒3区温度 482 到 500°F 250 到 260°C

料筒4区温度 482 到 500°F 250 到 260°C

口模温度 446 到 464°F 230 到 240°C

挤出机螺杆长径比L / D > 28:1 > 28:1

挤压说明

Head pressure: P > 140 bar / 2000 psi; Fine screen packs as needed

Screw Speed: RPM > 50% nominal

Screw design:

• Multi-purpose or barrier screw with mixing section 

• Screw diameter > 60 mm / 2.5 in 

 

Grooved Feed: Hot temperature: 120°C (212°F)

 

 

 

 

 

 